The diffusion coefficient for aluminum in silicon is D_Al in Si = 3 times 10^- 16 cm^2/s at 300 K. What is a reasonable value for D_Al in Si at 600 K? 1.5 times 10^-16 cm^2/s 3 times 10^-16 cm^2/s 6 times 10^-16 cm^2/s 1.5 times 10^-16 cm^2/s > 6 times 10^-16 cm^2/s